Synthesis Of Biofoam Based On Glucomannan Porang And Polyvinyl Alcohol (PVA) With The Addition of Seaweed Dregs

Abstract

Biofoam (Biodegradable foam) is an alternative packaging to Styrofoam made from natural raw materials that can be biodegraded in the soil. Biofoam is generally made from 3 constituent materials in the form of main ingredients in the form of starch or other similar materials, plasticizers such as PVA and also fillers in the form of fibers containing cellulose. The purpose of this study was to determine the effect of the combination of porang glucomannan, PVA and seaweed pulp on biofoam and to determine the best formulation and characteristics of the biofoam samples made.. The technique of making biofoam was done using baking technique with 9 different treatments. Each treatment was repeated 3x and observations were made on biofoam structure, mechanical properties testing (tensile strength, elongation and young modulus), water absorption test, and biodegradation test. The results showed that Polyvinyl Alcohol plays a role in the formation of a hollow biofoam structure. The thickness parameter value for each treatment was 0.628-1.939 mm. The tensile strength value of each treatment has a value ranging from 15.989-35.265 N/mm². The elongation value for each treatment ranged from 25.719-76.427%. The young modulus value for each treatment ranged from 0.343-0.896 N/mm². The water absorption value of each treatment obtained values ranging from 35.81-77.12%. And the value of testing biodegradation parameters obtained values ranging from 8.68-32.18%. So that the best treatment obtained using the multiple attribute method is the A3B1 treatment (PVA 15% and the ratio of seaweed pulp concentration to glucomannan 1: 2).

Full Text:

PDF

References

Aprilianti, N., Hajrah, H., & Sastyarina, Y. (2020). Optimasi Polivinil alkohol (PVA) Sebagai Basis Sediaan Gel Antijerawat. Proceeding of Mulawarman Pharmaceuticals Conferences, 11, 17–21.

Arizal, V., Darni, Y., Azwar, E., Lismeri, L., & Utami, H. (2017). Aplikasi Rumput Laut Eucheuma Cottonii Pada Sintesis Bioplastik Berbasis Sorgum Dengan Plasticizer Gliserol. Prosiding Dalam Rangka Seminar Nasional Riset Industri Ke 3 Balai Riset Dan Standardisasi Industri Bandar Lampung, September, 32– 39.

Darni, Y., Amalia, F., Azwar, E., Utami, H., Lismeri, L., & Haviz, M. (2022). Pemanfaatan Jerami Padi sebagai Filler dalam Pembuatan Biodegradable Foam (Biofoam). Jurnal Teknologi Dan Inovasi Industri, 03(02), 18–026.

Dzaky, M., Sulmartiwi, L., & Pujiastuti, D. Y. (2022). Application of Modified Starch on Bioplastic Spoon Based Carrageenan from Eucheuma cottonii on Biodegradability and Water Resistance. Journal of Marine and Coastal Science, 11(2), 40–48.

Firmansyah, Y. W., Fuadi, M. F., Ramadhansyah, M. F., Sugiester S, F., Widyantoro, W., Lewinsca, M. Y., Diyana, S., Marliana, N. I. V., Arumdani, I. S., Pratama, A. Y., Azhari, D., Sukaningtyas, R., & Hardiyanto, A. (2021). Keberadaan Plastik di Lingkungan, Bahaya terhadap Kesehatan Manusia, dan Upaya Mitigasi: Studi Literatur. Jurnal Serambi Engineering, 6(4), 2279-2285.

Fitrianti, Y., Azzahra, R. T., Kusumawati, E., & Keryanti. (2023). Pengaruh Penambahan Polyvinyl Alcohol (PVOH) pada Biofoam dari Tepung Biji Nangka dan Ampok Jagung dengan Metode Thermopressing. Jurnal Teknik Kimia USU, 12(2), 100–107.

Haiqal, H., & Muldarisnur, M. (2023). Analisis Sifat Fisis dan Mekanik Biodegradable Foam Berbahan Dasar Selulosa Jerami Padi dan Polivinyl Alcohol. Jurnal Fisika Unand, 12(4), 621–627.

Hevira, L., Ariza, D., & Rahmi, A. (2021). Pembuatan Biofoam Berbahan Dasar Ampas Tebu dan Whey. Jurnal Kimia Dan Kemasan, 43(2), 75–81.

Lestari, M. D., Sudarmin, & Harjono. (2018). Ekstraksi Selulosa dari Limbah Pengolahan Agar Menggunakan Larutan NaOH sebagai Prekursor Bioetanol. Indonesian Journal of Chemical Science, 7(3), 236–241.

Marlina, R., Sumantri, Y., Kusumah, S. S., Syarbini, A., Cahyaningtyas, A., Petanian, T. I., Ilmu, F., Halal, P., & Djuanda, U. (2021). Karakterisasi Komposit Biodegradable Foam Dari Kemasan Pangan. Jurnal Kimia Dan Kemasan, 43(1), 1–11.

Limbong, S. F., Harsojuwono, B. A., & Hartiati, A. (2022). Pengaruh Pengaruh Konsentrasi Polivinil Alkohol dan Lama Pengadukan Pada Proses Pemanasan terhadap Karakteristik Komposit Biotermoplastik Maizena dan Glukomanan. Jurnal Ilmiah Teknologi Pertanian Agrotechno, 7(1), 37.

Muhaimin, M. (2019). Plastik Biodegradable Dari Kulit Singkong Dengan Penambahan Serbuk Batang Tembakau. Universitas Jember.

Nurlatifah, I., & A. (2023). The Utilization from Glucomannan of Porang Flour ( Amorphophallus Muelleri Blume ) as a Raw Material for Making an Edible Film. Berkala Sainstek, 11(3), 138–144.

Pamela, V. Y., Syarief, R., Iriani, E. S., & Suyatma, N. E. (2017). Karakteristik Mekanik, Termal Dan Morfologi Film Polyvinil Alcohol Dengan Penambahan Nanopartikel ZnO Dan Asam Stearat Untuk Kemasan Multilayer. Jurnal Penelitian Pascapanen Pertanian, 13(2), 63.

Pratami, N. L. F. P., Hartiati, A., & Harsojuwono, B. A. (2021). Karakteristik Komposit Bioplastik dalam Variasi Rasio Pati Gadung (Dioscorea hispida D.) - Glukomanan dan Suhu Gelatinisasinya. Jurnal Rekayasa Dan Manajemen Agroindustri, 9(2), 166.

Putri, S. S., Harsojuwono, B. A., & Anggreni, A. A. M. . (2023). Pengaruh Konsentrasi Polivinil Alkohol dan Magnesium Stearat terhadap Karakteristik Bahan Pengemas Biokomposit Foam Tapioka dan Glukomanan. Jurnal Ilmiah Teknologi Pertanian, 8(2), 102–108.

Rachma, R. N., Hidayati, N., Rahayu, P., & Anggraini, H. (2021). Pengaruh Penambahan Zat Pemlastik Gliserol Terhadap Sifat Mekanik pada Pembuatan Bioplastik dari Kitosan - Umbi Porang (Amorphophallus Muelleri Blume).Jurnal Teknologi, 9(1), 13–22.

Reviandi, A. T., Harsojuwono, B. A., & Suhendra, L. (2022). Pengaruh Perbandingan Sorbitol dan TDI-80 Terhadap Karakteristik Biokomposit Foam 43 The Effect Ratio Of Sorbitol And TDI-80 On The Characteristics Of Cornstarch-Glucomannan Foam Biocomposite Abstrak. Jurnal Ilmiah Teknologi Pertanian, 7(2), 153–159.

Sari, N., Mairisya, M., Kurniasari, R., & Purnavita, S. (2019). Metana : Media Komunikasi Rekayasa Proses dan Teknologi Tepat Guna Bioplastik Berbasis Galaktomanan Hasil Ekstraski Ampas Kelapa Dengan Campuran Polyvinyl Alkohol. Metana : Media Komunikasi Rekayasa Proses Dan Teknologi Tepat Guna, 15(2), 71–78.

Sarlinda, F., Hasan, A., & Ulma, Z. (2022). Pengaruh Penambahan Serat Kulit Kopi dan PVA terhadap Karakteristik Biodegradable Foam dari Pati Kulit Singkong. Jurnal Pengendalian Pencemaran Lingkungan (JPPL), 4(2), 9–20.

Wardana, A. A. (2016). Pembuatan Pelapis Bionanokomposit Tapioka, Nanopartikel ZnO dan Asam Stearat Serta Aplikasinya pada Mangga Terolah Minimal. Thesis. Institut Pertanian Bogor, 1–51.

Warlani, L. (2019). Pengelolaan Sampah Plastik Untuk Mitigasi Bencana Alam. Seminar Nasional FST Universitas Terbuka, 89–110

Wening, D. N., & Amalia, R. (2023). Optimasi Kondisi Operasi Pembuatan Plastik Biodegradable dari Selulosa Tongkol Jagung dan Pati Kulit Singkong dengan Penambahan PVa dan TiO 2 sebagai Smart Packaging. Rekayasa Proses, 17(1), 1–9.

Zulmanwardi, & Sofia, I. (2023). Pemanfaatan Pati Ubi Uwi ( Deoscorea alata ) Dan Limbah Jerami Padi ( Oryza sativa ) Sebagai Bahan Baku Alternatif Biofoam (Biodegradable Foam). 9(1), 1104–1111.

DOI: https://doi.org/10.46676/ij-fanres.v5i3.385

Refbacks

• There are currently no refbacks.

E-ISSN : 2722-4066

This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.